Col-GAG and MC-GAG scaffolds were prepared using lyophilization, as described previously (3739). Briefly, microfibrillar, type I collagen (Collagen Matrix, Oakland, NJ) and chondroitin-6-sulfate (Sigma-Aldrich, St. Louis, MO) were combined in suspension in the absence and presence of calcium salts (calcium nitrate hydrate, Ca(NO3)2·4H2O; calcium hydroxide, Ca(OH)2; Sigma-Aldrich, St. Louis, MO) in an acetic acid (Col-GAG) or phosphoric acid (MC-GAG) solution. Using a constant cooling rate technique at a rate of 1°C/min, the solution was frozen from room temperature to −10°C using a freeze dryer (Genesis, VirTis). Following sublimation of the ice phase, scaffolds were sterilized via ethylene oxide and cut into 8-mm disks in diameter and 4 mm in height for culture.

Cross-linking of scaffolds was performed after rehydration in phosphate-buffered saline (PBS) for 4 hours using 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDAC; Sigma-Aldrich) and N-hydroxysuccinimide (NHS; Sigma-Aldrich) at a molar ratio of 5:2:1 EDAC:NHS:COOH, where COOH represents the amount of collagen in the scaffold as we previously described (40). Scaffolds were washed with PBS to remove any of the residual chemical.

Note: The content above has been extracted from a research article, so it may not display correctly.



Q&A
Please log in to submit your questions online.
Your question will be posted on the Bio-101 website. We will send your questions to the authors of this protocol and Bio-protocol community members who are experienced with this method. you will be informed using the email address associated with your Bio-protocol account.



We use cookies on this site to enhance your user experience. By using our website, you are agreeing to allow the storage of cookies on your computer.